Barium Titanate (Temperature dependence)
Barium Titanate (Temperature dependence)
The sample( Single crystal BariumTitanate) was heated from room temperature to Curie point and was cooled back. During the process domains were studied.
Device:
NTEGRA Prima
Tip:
DCP20
Barium Titanate (Temperature dependence)
size:
10x10 um
SPM principle:
Piezoresponse Force Microscopy
Domain picture at T = 50 °С (Heating)
size:
10x10 um
Domain picture at T = 75 °С (Heating)
size:
10x10
SPM principle:
Piezoresponse Force Microscopy
Domain picture at T = 150 °С (Heating)
size:
10x10 um
SPM principle:
Piezoresponse Force Microscopy
Domain picture at T = 75 °С (Cooling)
size:
10x10 um
SPM principle:
Piezoresponse Force Microscopy
Topography
size:
10x10 um
SPM principle:
Piezoresponse Force Microscopy
PMN-PZN-PT
Polished and etched SrTiO3
Остались вопросы? Позвоните нам по телефону: +7-499-110-2050
или заполните форму обратной связи, и мы ответим на все интересующие Вас вопросы.
Спросить эксперта
Отправить запрос
Для технической поддержки используйте
Онлайн сервис
* - Требуется заполнить.
Отправить
Принять политику конфиденциальности